The kind of fiberglass sleeving is the E-fiberglass braided sleeving coated with polyviny1 chloride resin.It is produced with the process of thermoplasticization.
The polyviny1 chloride fiberglass sleeving possesses good qualities of dielectric,chemical resistance,excellent softness and elasticity.It can be used for wiring insulation and mechanical protection for electrical machinery,electric appliances,electrcial instruments and apparatus,wireless sets,TV sets and domestic electrical appliances of electrical fans,washing machine etc. |
|
|
|
| Specifications︰ |
| Bore Diameter |
Wall Thickness |
| Nominal |
Tolerance （±） |
Minimum |
Maximum |
| 0.5,0.8 |
±0.10 |
0.20 |
0.50 |
| 1.0,1.5 |
±0.15 |
0.20 |
0.75 |
| 2.0,2.5 |
±0.20 |
0.20 |
0.75 |
| 3.0 |
±0.25 |
0.20 |
0.75 |
| 3.5,4.0,5.0 |
±0.25 |
0.30 |
0.75 |
| 6.0 |
±0.25 |
0.30 |
1.00 |
| 7.0,8.0 |
±0.50 |
0.30 |
1.00 |
9.0,10.0,12.0,14.0,16.0
18.0,20.0,23.0,25.0,27.0 |
±0.50 |
0.40 |
1.30 |
|
| Advantages︰ |
| Property |
Requirements |
| Bending after heating |
No cracking or detachment of coating shall be visible after bending around mandrels after 96h at 130degreee |
| Bending at low temperature |
No cracking or detachment of coating shall be visible after bending around mandrels while at -25degree |
| Temperature index(degree) |
105 |
| Breakdown Voltage,KV |
≥4.0KV( Room temp ) |
|
| Export Markets︰ | Domestic \ Europe and the United States |
| Standard Met︰ | JB/T 8151.2―1999 |
|
|
|