| Glass textile sleeving with silicone elastomer coating produced with the process of thermal treatment and vulcanization is the non-alkali fiberglass braided sleeving coated with silicone rubber. This sleesivng possesses good qualities of dielectric, high temperature resistance. It can be used for wiring insulation and mechanical protection for electrical machinery and electrical appliances. |
|
|
|
| Specifications︰ |
| Bore Diameter |
Wall Thickness |
| Nominal (mm) |
Tolerance （±） |
Minimum |
Maximum |
| 0.5,0.8 |
±0.10 |
0.20 |
0.50 |
| 1.0,1.5 |
±0.15 |
0.20 |
0.75 |
| 2.0,2.5,3.0 |
±0.20 |
0.20 |
0.75 |
| 3.5,4.0,5.0,6.0 |
±0.25 |
0.30 |
0.75 |
| 7.0,8.0,9.0,10.0 |
±0.25 |
0.30 |
1.10 |
| 12.0,14.0,16.0,18.0,20.0,23.0 |
±1.00 |
0.40 |
1.20 |
| 25.0,27.0,30.0 |
±1.00 |
0.40 |
1.40 |
|
| Advantages︰ |
| Property |
Requirements |
| Elasticity |
no cracking or detachment of coating shall be visible
1、 after 3hours at 200 ± 2℃
2、 after 2hours at - 40~ -60℃ |
| Flame propagation method |
≤60 s |
| Heat resistance |
No cracking detachment of coating shall be visible after 72hours at 200± 5℃ |
| Breakdown voltage |
≥ 2.5KV( at room temperature ) |
| Insulation resistance |
≥ 10 9Ω |
|
|
|
|